PolyTerra™ PLA (1.75 mm, 1 kg)(Sapphire Blue)

PolyTerra™ PLA (1.75 mm, 1 kg)(Sapphire Blue)

CAD $27.99 CAD $24.50 Save CAD $3.49
/
  • In stock, ready to ship
  • Inventory on the way

All in-stock orders from InkSmith are fulfilled within 1-3 business days from our facility in Waterloo, Ontario (unless otherwise specified for product pre-orders). 

Orders are accompanied with a tracking number at the time of fulfillment.

This site is protected by reCAPTCHA and the Google Privacy Policy and Terms of Service apply.

 

PolyTerra™️ PLA by PolyMaker™️ is a bioplastic based 3D printing filament designed from the ground up to create the next generation of PLA, providing ease of use, printing quality, speed and reliability. It is a sustainable product sourced naturally and for every spool produced a tree is planted to give back to the earth.

  • PRINTS FASTER THAN REGULAR PLA
  • EASY SUPPORT REMOVAL
  • SMOOTH MATTE SURFACE FINISH
  • RECYCLED CARBOARD PACKAGING AND SPOOL
  • PLANT ONE TREE FOR EVERY SPOOL SOLD
  • TOUGHER THAN REGULAR PLA

PolyTerra™️ prints just like regular PLA. Overhang and bridging functions can even outperform PLA. With a wide printing temperature range from PolyTerra™️ can be processed on any extrusion-based 3D printer.

The mechanical properties of PolyTerra™️ offer a wide range of applications as the material is tougher than normal PLA while still retaining good rigidity.

Young’s Modulus:
1882 ± 141 Mpa

Tensile Strength:
20.9 ± 2.0 Mpa

Bending Strength:
39.6 ± 1.1 Mpa

Charpy Impact Strength:
5.7 ± 0.4 kJ/m2

Glass Transition Temperature:
60.6˚C

Vicat Softening Temperature:
62.7˚C

Melting Temperature:
162.6˚C

Drying Settings:
55˚C for 6h

Recommended Support Materials:
PolyDissolve™ S1, PolySupport™

  NET WEIGHT: 1 KG (2.2 LB)

 

 Printing Temperature:

Note:
190°C - 230°C

Printing Speed:
30mm/s – 70 mm/s

Bed Temperature:
25˚C – 60˚C

Bed Surface:
Glass, Blue Tape, BuilTak®

Cooling Fan:
ON

Drying Settings:
55˚C for 6h

Recommended Support Materials:
PolyDissolve™ S1, PolySupport™